Alcohol wet milling of calcium hydroxide and apatite
Alcohol wet milling of calcium hydroxide and apatite. Calcium hydroxide: D50 4.31 µm, D90 8.37 µm; apatite: D50 1.91 µm, D90 3.48 µm; each at 2.5 hours.
Sample trials.
Explore the material, the setup and the measured result.
117 sample trials
View record
Ferrite powder: recorded D50 reduction from 3.5 to 0.6 µm
Ferrite powder: recorded D50 reduction from 3.5 to 0.6 µm. D50 = 0.6 µm; D90 = 3.3 µm after two hours of milling.
- D50
- 0.6 µm
- D90
- 3.3 µm
Two slag samples meet a recorded specific-surface-area objective
Two slag samples meet a recorded specific-surface-area objective. Fly-ash slag: 862.489 m²/kg at ten minutes; manganese slag: 916.314 m²/kg at 30 minutes, units from the objective.
Air-cooled ammonium-bicarbonate wet milling to D50 9.4 µm
Air-cooled ammonium-bicarbonate wet milling to D50 9.4 µm. D50 = 9.4 µm; D90 = 18.2 µm at 60 minutes; later 20-minute extension unmeasured.
- D50
- 9.4 µm
- D90
- 18.2 µm
Diamond powder: measured reduction during a one-hour planetary trial
Diamond powder: measured reduction during a one-hour planetary trial. Planetary sample at 60 minutes: D50 = 0.6 µm; D90 = 2.48 µm.
- D50
- 0.6 µm
- D90
- 2.48 µm
Licorice reaches powder form and complete 50-mesh passage in a planetary trial
Licorice reaches powder form and complete 50-mesh passage in a planetary trial. Planetary stage at 60 minutes: powder formed; complete passage through a 50-mesh sieve.
Quartz sand dry milling to an accepted D50 endpoint
Quartz sand dry milling to an accepted D50 endpoint. D50 = 12.3 µm; D90 = 30.5 µm at 150 minutes.
- D50
- 12.3 µm
- D90
- 30.5 µm
Kaolin wet milling with a mixed zirconia-ball charge
Kaolin wet milling with a mixed zirconia-ball charge. D90 = 1 µm in the result field; total recorded run 50 minutes, exact sample association unspecified.
- D90
- 1 µm
Air-cooled green-tea trials meet a D60 objective
Air-cooled green-tea trials meet a D60 objective. Sample 1: D60 = 8.9 µm; sample 2: D60 = 11.3 µm at their recorded later checkpoints.
Carbon powder meets a D90 interval in a short dry planetary trial
Carbon powder meets a D90 interval in a short dry planetary trial. D50 = 3.2 µm; D90 = 7.29 µm after 30 minutes.
- D50
- 3.2 µm
- D90
- 7.29 µm
Silica and glass mixture: mixing with progressive particle-size reduction
Silica and glass mixture: mixing with progressive particle-size reduction. D90 = 9.7 µm, recorded 180-minute checkpoint.
- D90
- 9.7 µm
Nickel-powder flaking: recorded attainment after separate twenty-four-hour planetary trials
Nickel-powder flaking: recorded attainment after separate twenty-four-hour planetary trials. Convert the powders to flake morphology.
Results apply to the sample and conditions tested. Review each record for its setup and measurement notes.