Rhodium powder trial recorded as reaching 325 mesh in three hours
Rhodium powder trial recorded as reaching 325 mesh in three hours. Meet the stated 325-mesh requirement.
Sample trials.
Explore the material, the setup and the measured result.
117 sample trials
View record
Bone wet milling: two twenty-minute samples with recorded D50 and D90
Bone wet milling: two twenty-minute samples with recorded D50 and D90. Observe the response; no numerical acceptance target was entered.
Battery-material powder: a favorable two-hour planetary sample
Battery-material powder: a favorable two-hour planetary sample. Observe the milling response; no numerical size target was recorded.
Alumina wet planetary trial recorded as meeting D90 = 6 µm at two hours
Alumina wet planetary trial recorded as meeting D90 = 6 µm at two hours. Meet the specifically stated D90 = 6 µm requirement.
Ferrite wet planetary trial favorably compared with an earlier corundum-jar run
Ferrite wet planetary trial favorably compared with an earlier corundum-jar run. Observe the grinding response; no numerical size criterion was entered.
Barite planetary trial recorded as meeting an 800-mesh requirement at three hours
Barite planetary trial recorded as meeting an 800-mesh requirement at three hours. Meet the stated 800-mesh requirement.
Magnesium oxide: recorded acceptance after a thirty-minute planetary trial
Magnesium oxide: recorded acceptance after a thirty-minute planetary trial. Observe the milling response and obtain an acceptable sample; no numerical fineness target was entered.
Pharmaceutical powder trial recorded as meeting 100 mesh in two minutes
Pharmaceutical powder trial recorded as meeting 100 mesh in two minutes. Meet the recorded 100-mesh requirement.
Silicon nitride planetary samples: recorded acceptance at three hours
Silicon nitride planetary samples: recorded acceptance at three hours. Observe the milling response and obtain an acceptable sample; no numerical target was entered.
Rice powder formation: a first trial and a thirty-minute repeat
Rice powder formation: a first trial and a thirty-minute repeat. Convert the rice to powder.
Tungsten ore wet trial: recorded acceptance and a two-hour D90 reading
Tungsten ore wet trial: recorded acceptance and a two-hour D90 reading. Meet the recorded 1 µm fineness requirement.
Copper chips: complete 50-mesh sieve passage after the recorded speed increase
Copper chips: complete 50-mesh sieve passage after the recorded speed increase. Meet a 50-mesh requirement.
Results apply to the sample and conditions tested. Review each record for its setup and measurement notes.